Double Coated Tissue Tape 1110
1. Description:  
Cleanly removable low-VOC  (Volatile Organic Compounds) double  coated  tape #1110 has  special  high  strength  tissue
backing with acrylic adhesive on both sides. #1110 provides high adhesion  to  a wide variety of materials  and  it  can be
removed with minimum residuals on the substrate without tissue break after long term after bonding. 14 substances*1

specified by Health, Labor and Welfare Ministry in Japan are not intentionally used for the tape. The amount of VOCs*2

that causes sick house syndrome is very low from the tape.  
*1: Formaldehyde, Toluene, Xylene, Paradichlorobenzene, Ethyl benzene, Styrene, Cholorpyrifos, Di-n-butyl  phthalate,  Tetradecan,  Nonanal,  Di-2-ethylhexyl  phthalate,
Diazinon, Acetaldehyde, Fenobucarb, 14 substances.
*2: object substance of above guideline

2. Structure:  








3. Key Features:  
(1) Strong adhesion to various substrates
(2) Clean removable from substrates without tissue backing break
(3) Low amount of VOC evaporated from the tape
4. Applications:  
(1) Bonding of films or foams inside electronic devices
(2) Decoration materials attachment for electric appliance
(3) Metal or plastic nameplate attachment
(4) Interior base sheet fixing for automotive
(5) Cushion attachment for toys, musical instruments, leisure gears, etc.
Adhesive: Acrylic
Backing: Special high strength tissue
Adhesive:  Acrylic

Release liner: Silicone treated flat paper 



2/3
5. General Properties:
Product name  1110
Tape  Colorless opaque
Color
Liner
White
(With “3M Low VOC” logo)
Tape  0.150  Thickness
(mm)  Liner  0.110
Length direction  16.5  Tensile strength
(N/cm)  Width direction  13.7
180 degree peel adhesion (N/cm)  8.2
Dynamic shear strength (N/c㎡)  169.0
        
Test Method
Thickness: Using thickness gauge with caliper foot of 5mm diameter (JIS S 0237)
Tensile strength:  
Distance between chucks: 100 mm, testing speed: 300 mm/min
180 degree peel adhesion:
To stainless steel  (SUS 304 BA), support material: 0.025mm PET,  lamination: 2 kg  rubber  roller once
for each direction, dwell: 20-40 minutes at RT, testing speed: 300 mm/min
Dynamic Shear Strength:
To stainless steel (SUS 304 BA), lamination: 5 kg rubber roller once in each direction, dwell: 24 hours
at RT, testing speed: 300 mm/min
6. 180 Degree Peel Adhesion to Various Substrates (N/cm):